| Physical Properties Table of PP composite Plastic materials |
|
|
| Test items | Test method | Unit | RG6020 | RG6030 | RG6050 | RG6030S | RT6020 | RT6040 | PT612 | 608S |
| Properties | Test Condition | Unit |
| Density(Specific gravity)
| D792 | g/cm3 | 1.04 | 1.12 | 1.32 | 1.10 | 1.04 | 1.22 | 1.02 | 0.9 |
| Specific Gravity |
| Molding shrinkage rate | - | % | 0.8 | 0.7 | 0.6 | 0.7 | 1.5 | 1.2 | 1.2~1.6 | 1.5~1.7 |
| Mold Shrinkage |
| @Flow(3.2mm)
|
| Tensile strength | D638 | kg/cm2
| 850 | 1400 | 1700 | 1250 | 350 | 420 | 155 | 180 |
| Tensile Strength +23˚C
| Mpa | 85 | 140 | 170 | 125 | 35 | 42 | 15.5 | 18 |
| Elongation at break | D638 | % | 5 | 4 | 3 | 5 | 60 | 20 | 60 | 150 |
| Elongation at Break +23˚C
|
| Flexural modulus | D790 | kg/cm2
| 42000 | 56000 | 98000 | 53000 | 25000 | 40000 | 11000 | 11050 |
| Flexural Modulus +23˚C
| Mpa | 4200 | 5600 | 9800 | 5300 | 2500 | 4000 | 1100 | 1105 |
| Heat distortion temperature | D648 | ˚C | 150 | 158 | 162 | 152 | 110 | 122 | 105 | 106 |
| Heat Deflection |
| Temperature 4.6kg/cm2
|
| Ehrlich impact strength IZOD Impact Strength, Notched(3.2mm) | + 23˚C
| D256 | kg.cm/cm | 8 | 10 | 14 | 16 | 4 | 4 | 34 | 54 |
| lb.ft/in | 1.4 | 1.8 | 2.5 | 2.9 | 0.7 | 0.7 | 6.1 | 9.7 |
| - 20˚C
| D256 | kg.cm/cm | - | - | - | - | - | - | 14 | - |
| lb.ft/in | - | - | - | - |
| - | 2.5 |
|
| Flammability (1.6mm)
| UL-94 |
| HB | HB | HB | HB | HB | HB | HB | HB |
| Flammability UL-94 |
| Ash content | - | % | 20 | 30 | 50 | 30 | 20 | 40 | - | - |
| ASH |
| "Preparation note | 20%GF Strengthen
| 30%GF Strengthen
| 50%GF Strengthen
| 30%GF Strengthen cold resistance
| 20%mine Fiber reinforcement
| 40%mine Fiber reinforcement
| Automobile Accessories
| Automobile Accessories
|
|
|
|
|
|
|
|
|
|
|
|
|
| The physical property values listed in this table are for reference only and are not guaranteed values |
|
|
| All figures entered in this table are typical figures and therefore no guarantee |
|
|
|